A wide range of epoxy resins are molded to produce composite components for various applications. Release agents are generally used to facilitate the removal of the component from the mold. The work presented in this paper shows differences between release agents and resin during a RTM process. Adhesive properties of release agents in interaction with the resin are analyzed, with respect to pressure and temperature. It was found that the reaction of epoxy resin results in different breakaway forces from mould surfaces depending on used agents.Keywords
Array
Array
Array
Array
Array
DOI:
10.5937/jaes13-7210
References
Autori koji objavljuju u ovom časopisu pristaju na sledeće uslove:
- Autori zadržavaju autorska prava i pružaju časopisu pravo prvog objavljivanja rada i licenciraju ga Creative Commons licencom koja omogućava drugima da dele rad uz uslov navođenja autorstva i izvornog objavljivanja u ovom časopisu.
- Autori mogu izraditi zasebne, ugovorne aranžmane za neekskluzivnu distribuciju rada objavljenog u časopisu (npr. postavljanje u institucionalni repozitorijum ili objavljivanje u knjizi), uz navođenje da je rad izvorno objavljen u ovom časopisu.
- Autorima je dozvoljeno i podstiču se da postave objavljeni rad onlajn (npr. u institucionalnom repozitorijumu ili na svojim internet stranicama) pre i tokom postupka prijave priloga, s obzirom da takav postupak može voditi produktivnoj razmeni ideja i ranijoj i većoj citiranosti objavljenog rada (up. Efekat otvorenog pristupa).
Downloads
Download data is not yet available.