To improve the wear resistance of γ-TiAl alloy, Ta alloy layer was prepared on surface by double glow plasma surface alloying technique. The tribology behavior of Ta alloy layer against Si3N4 at 25℃, 350℃ and 500℃ were comparatively studied. The results showed that Ta alloy layer comprised a deposition layer and a diffusion layer. The deposition layer played a role in protection as a soft film. With the increase of temperature, the wear mechanism of γ-TiAl changed from abrasive wear to coexistence of abrasive wear and oxidation wear. Ta alloy layer’s wear mechanism changed from adhesive wear to coexistence of adhesive wear and oxidation wear. Surface Ta alloying process significantly reduced the wear volume, the specific wear rate and the friction coefficient of γ-TiAl and improved the wear resistance properties of γ-TiAl.
Keywords
Array
Array
Array
References
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.