The NiCr/YSZ coating was fabricated on γ-TiAl alloy by double glow plasma surface metallurgy technology and multi-arc ion plating technology. The microstructure, microhardness, bonding strength and burn resistance of NiCr/YSZ coating were studied in detail. The results showed that the NiCr/YSZ coating was dense and homogeneous, including a duplex structure of top YSZ ceramic coating and underlying Ni-Cr bond coating. The average microhardness of NiCr/YSZ coating was raised by a factor of about 2 compared to the γ-TiAl substrate. The thermal shock test indicated that the composite structure had superior bonding strength and the defects such as metal droplets on the ceramic coating were the source of cracks. The high-energy laser beam destroyed the surface of γ-TiAl alloy, forming protruding combustion products in ablation zone and splashing residues around ablation zone. When coated by NiCr/YSZ coating, the combustion process was delayed through isolating and dissipating heat. The ablation range was controlled and the ablation damage was reduced at the same irradiation power. The NiCr/YSZ coating preliminarily realized to improve the burn resistance of γ-TiAl alloy.
Keywords
Array
Array
Array
Array
References
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.