Abstract
In this work, a new Mg-2Zn-0.8Sr-0.2Ca alloy with low content of alloying elements was subjected to extrusion at relatively low-temperatures (240 and 200°C) and slow-speed (1.0 mm/s and 0.1 mm/s). The average size and volume fraction of recrystallized grains in the extruded Mg-2Zn-0.8Sr-0.2Ca alloy gradually decreased with the reduction in extrusion rate or extrusion temperature. Some broken second phases including Ca2Mg6Zn3 and Mg17Sr2 appeared in the extruded Mg-2Zn-0.8Sr-0.2Ca alloy along with some precipitated nano-sized MgZn2 phases. The volume fraction of MgZn2 phases gradually in the alloy increased as extrusion rate or temperature decreased. High performance with yield strength of 393.1 MPa, ultimate tensile strength of 418.4 MPa and the elongation of 5.7% was obtained in the Mg-2Zn-0.8Sr-0.2Ca alloy extruded at 200°C & 0.1 mm/s. The main strengthening mechanisms could be attributed to grain-boundary strengthening, dislocation strengthening, precipitation strengthening, which were related to the change in grain size, second phases and basal texture intensity for the extruded Mg-2Zn-0.8Sr-0.2Ca alloy.
Keywords
References
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.