Abstract
The present paper analyzes the effect of low aluminum additions and the hot forging process on the microstructure and non-metallic inclusions of high manganese steels. Four high-manganese steels (HMnS) were obtained by adding low aluminum contents of 1.1 and 1.5 wt. % in four medium carbon austenitic steels (0.3 - 0.4 wt. % C) with manganese contents of 17 and 22 wt. Samples of the as-cast steels were hot forged to 1100 °C to obtain a whole reduction of 70 %. The microstructural evolution was studied by microscopy techniques (OM, and SEM-EDS) and X-Ray diffraction measurements for the as-cast and hot forged steels. A typical grain columnar zone obtained during solidification of an ingot casting was obtained in the as-cast condition where the microstructure was constituted by non-metallic inclusions in a fully austenitic matrix. The non-metallic inclusions were identified as Al2O3 and MnS particles. The thermomechanical treatment allows the formation of an austenitic microstructure characterized by twins in high manganese steels while a duplex austenitic-martensitic microstructure was obtained for HMnS which contained the lowest manganese contents. The highest tensile properties were obtained for the steel 17Mn-1Al which showed the lowest grain size and finer non-metallic inclusions content. The hardness values were similar to those obtained in the as-cast condition.
Keywords
References
Authors retain copyright of the published papers and grant to the publisher the non-exclusive right to publish the article, to be cited as its original publisher in case of reuse, and to distribute it in all forms and media.
The Author(s) warrant that their manuscript is their original work that has not been published before; that it is not under consideration for publication elsewhere; and that its publication has been approved by all co-authors, if any, as well as tacitly or explicitly by the responsible authorities at the institution where the work was carried out. The Author(s) affirm that the article contains no unfounded or unlawful statements and does not violate the rights of others. The author(s) also affirm that they hold no conflict of interest that may affect the integrity of the Manuscript and the validity of the findings presented in it. The Corresponding author, as the signing author, warrants that he/she has full power to make this grant on behalf of the Author(s). Any software contained in the Supplemental Materials is free from viruses, contaminants or worms.The published articles will be distributed under the Creative Commons Attribution ShareAlike 4.0 International license (CC BY-SA).
Authors are permitted to deposit publisher's version (PDF) of their work in an institutional repository, subject-based repository, author's personal website (including social networking sites, such as ResearchGate, Academia.edu, etc.), and/or departmental website at any time after publication.
Upon receiving the proofs, the Author(s) agree to promptly check the proofs carefully, correct any typographical errors, and authorize the publication of the corrected proofs.
The Corresponding author agrees to inform his/her co-authors, of any of the above terms.